With outstanding physical chemical and electrical property it widely used for electrical insulation bunding to prevent corrosion and provid mechanical protection3:1 shrink ratio more suitable for application to lrregular awkward shapes.
·Very flexibie highly flame retardant(except clear)
·Operating temperature:-55℃to+135℃
·Minimum shrink temperature:70℃
·Minimum fully recovery temperature:105℃
·Standard color: Black S
·pecial color: Red Blue Yellow Green Clear (class2)
|
Property
|
Test Method
|
Typical Data
|
|
Tensile strength
|
ASTM D 2671
|
14Mpa
|
|
Elongation at break
|
ASTM D 2671
|
800%
|
|
Tensile strength after aging(175℃/168hrs)
|
ASTM D 2671
|
14Mpa
|
|
Elongation after aging(175℃/168hrs)
|
ASTM D 2671
|
350%
|
|
Flammability
|
UL 224 VW-1
|
Pass
|
|
Heat shock(250℃/4hrs)
|
ASTM D 2671
|
No Cracking
|
|
Cold bend test(-55℃/4hrs)
|
ASTM D 2671
|
No Cracking
|
|
Dielectric strength
|
ASTM D 150
|
20kv/mm
|
|
Volume resistance
|
ASTM D 876
|
1014Ω.cm
|
|
Copper corrosion
|
UL 224
|
Pass
|
|
Water absorption
|
ASTM D 570
|
0.12%
|
|
Chemical resistance
|
ASE-AMS-DTL-23053/5
|
Pass
|
|
Longitudinal shrinkage
|
UL 224
|
0±5%
|
|
Eccentricity
|
UL 224
|
>30%
|
|
RCDRS Product Dimensions (3:1)
|
|
Normal size
|
As supplied(mm)
|
After recovered(mm)
|
Standard length(m/spool)
|
|
(mm)
|
(inch)
|
Inside diameter(Min)
|
Inside diameter(Max)
|
Wall thickness(Min)
|
|
RCDRS-15/0.5
|
1/16
|
1.6
|
0.5
|
0.45
|
200
|
|
RCDRS-3.0/1.0
|
1/8
|
3.2
|
1.0
|
0.55
|
200
|
|
RCDRS-4.5/1.5
|
3/16
|
4.8
|
1.5
|
0.60
|
100
|
|
RCDRS-6.0/2.0
|
1/4
|
6.4
|
2.0
|
0.65
|
100
|
|
RCDRS-9.0/3.0
|
3/8
|
9.5
|
3.0
|
0.75
|
100
|
|
RCDRS-12.0/4.0
|
1/2
|
12.7
|
4.0
|
0.80
|
50
|
|
RCDRS-18.0/6.0
|
3/4
|
19.1
|
6.0
|
0.90
|
50
|
|
RCDRS-24.0/8.0
|
1
|
15.4
|
8.0
|
1.20
|
50
|
|
RCDRS-39.0/13.0
|
11/2
|
39.0
|
13.0
|
1.25
|
50
|
|
RCDRS-50.0/17.0
|
2
|
51.0
|
17.0
|
1.30
|
50
|
|
RCDRS-60.0/20.0
|
21/2
|
65.0
|
20.0
|
1.35
|
50
|
|